PLCE100(A) PLCE100(A) heat-shrinkable cable caps are manufactured from a polyolefin material and coated with a hot-melt adhesive to provide a watertight seal against the damage of moisture, dirt or corrosion. PLCE100(A) will provide a seal at up to 0.05 Mpa internal pressure whilst operating between -55ºC to +110ºC. The rugged wall of these end caps also offers excellent resistance against abrasion
 |
 |
You will need to allow pop-ups on your browser
Overview
Up to 0.05Mpa Internal Pressure
Continuous Operating Temperature -55ºC to +110ºC
Optional Adhesive Liner
Good Chemical and Abrasion Resistance
PLCE100(A) heat-shrinkable cable caps are manufactured from a polyolefin material and coated with a hot-melt adhesive to provide a watertight seal against the damage of moisture, dirt or corrosion. PLCE100(A) will provide a seal at up to 0.05 Mpa internal pressure whilst operating between -55ºC to +110ºC. The rugged wall of these end caps also offers excellent resistance against abrasion
Technical
|
General
Installation temperature
Low temperature flexibility
|
125oC
14Mpa
|
|
Electrical
Dielectric strength
|
15kV/mm minimum
|
|
Thermal
Heat ageing
Elongation at Break
|
168 hours at 150oC
>300%
|
|
Flammability
Non flame retardant
|
|
Chemical
Fluid resistance
|
Fuels
Hydraulic fluids
Oils 23oC to ISO1817 |
|
Specifications
RoHS Compliant
|
|
Ordering
|
Ordering
Size (mm)
|
Minimum
ID Supplied (mm)
|
Maximum
ID Recovered (mm)
|
Length as
Supplied (mm)
|
Recovered
Wall Thickness (mm)
|
|
14/4
|
14.0
|
4.5
|
30
|
2.0
|
|
25/8
|
25.0
|
8.0
|
50
|
2.3
|
|
40/15
|
40.0
|
15.0
|
80
|
3.0
|
|
55/25
|
55.0
|
25.0
|
130
|
3.3
|
|
75/35
|
75.0
|
35.0
|
140
|
3.3
|
|
100/50
|
100.0
|
50.0
|
140
|
4.0
|
|
120/60
|
120.0
|
60.0
|
123
|
3.8
|
|
145/71
|
145.0
|
71.0
|
140
|
4.5
|
|
158/63
|
158.0
|
63.0
|
127
|
3.3
|
Standard colour: Black
Full details on technical specifications, test methods and values are available on request.